A Review on Engineering Transition Metal Compound Catalysts to Accelerate the Redox Kinetics of Sulfur Cathodes for Lithium–Sulfur Batteries

Highlights The representatively engineering strategies of cations/anions doping, bimetallic/bi-anionic transition metal compounds and heterostructure composites catalysts for lithium sulfur batteries are comprehensively reviewed. The promoted mechanism of catalytic performance by regulating electronic structure is focused on, including energy band, electron filling, d/p-band center, valence state. The superiority of the modified transition metal compounds is comprehensively summarized.


Introduction
Lithium-ion batteries are the most successful energy storage system developed in the past 30 years for their relatively high energy density and cycle stability.However, the limited theoretical energy density (420 Wh kg −1 ) of lithium ion batteries does not meet the requirements of some applications such as electric vehicles, and it has been urgent to develop high-performance batteries with higher energy density [1].Lithium-sulfur batteries (LSBs) have been widely concerned since 2009, when Nazar adopted mesoporous carbon as sulfur host, bringing its development possibility for high theoretical specific capacity of 1675 mAh g −1 and energy density of 2600 Wh kg −1 [2,3].Liquid electrolyte solves the sluggish kinetic of solid-solid reaction of LSBs from the initial S 8 directly to the final reaction product of the Li 2 S.However, challenges of LSBs come along with liquid electrolytes.Various intermediates lithium polysulfides (LiPSs, Li 2 S n , 2 ≤ n ≤ 8) are formed during multi-step charge-discharge process, and their solubility in the electrolyte causes their department from cathode materials [4].The infamous shuttle effect of LiPSs is formed in the electric field, which leads to the loss of sulfur species and capacity fading [5].
Since 2009, carbon materials represented by porous carbon have been used to physically adsorb LiPSs to mitigate the shuttle effect [6,7].Then, polar materials including doped carbon materials and various transition metal compounds (TMCs) with chemical interaction with LiPSs were introduced to sulfur cathodes, interlayers and modified separators [8,9].However, physical confinement with weak interaction and chemisorption strategy with limited adsorption sites are still not ideal to solve shuttle effect [2,10].Additionally, the chemisorption for LiPSs is not a determinant of the cathode performance [11].The conversion of S 8 → Li 2 S 8 is relatively easy and spontaneous, while the long-chain LiPSs are easily dissolved, and the transformation of Li 2 S 4 to Li 2 S 2 /Li 2 S requires high activation energy, which leads to the accumulation of LiPSs, and aggravate the shuttling effect.In addition, the transition from Li 2 S 2 to Li 2 S is slow in charge transfer kinetics due to its insulating properties, which is the most difficult stage and regarded as the rate-limiting step during discharging [12,13].During the charging stage, the oxidation of Li 2 S needs to overcome high energy barrier due to its slow kinetics, leading to the high overpotential [14].Therefore, the key factor of the shuttle effect is the sluggish reaction catalyst, and nanostructured metal-based catalysts.Among them, electrolyte mediators can effectively manipulate the conversion behavior of sulfur and Li 2 S such as reaction pathway, types of LiPSs, voltage polarization, Li 2 S deposition morphologies, and Li 2 S activation by controlling solvent species, LiPS dissolvability, salt species and concentration, addition of electrolyte additives as well as solid-state electrolytes.However, the electrolytic liquid system is complicated, and there are contradictions with the compatibility of lithium anodes, ionic conductivity, and viscosity [23].Non-metal materials like black phosphorus and functionalized carbon possess significant advantages in high specific surface area and light weight, the former is conducive to increasing the active area to promote the electrochemical reaction processes, and the latter is beneficial to improving the mass energy density of the battery.Unfortunately, black phosphorus only presents strong adsorption ability for LiPSs at the edge, but weak in the plane, showing the characteristics of edge selective catalysis [24].Similarly, the polar sites on the surface of modified carbon materials are limited.Moreover, the non-metal-Li bond formed between doped anions of functionalized carbon and Li of LiPSs does not play a key role for LiPSs adsorption as S-binding between metal atoms in TMCs and S atoms in LiPSs [25].Additionally, metal-based catalysts include supported single atom catalysts (SACs), metallic nanostructures, and TMCs.SACs with theoretical 100% atomic utilization, unsaturated coordination environment, and unique electronic structure are expected to achieve efficient catalysis for LSBs [1].However, SACs still suffer from the problem of poor stability, easy aggregation and low load due to their high surface energy.Nanostructured metal materials with sulfiphilicity, excellent conductivity and catalytic activity are another kind of excellent catalysts for LSBs [26].Alloys can effectively regulate its electronic structure with different metal elements, such as d-band center, thus improving the catalytic activity [27,28].However, the enhanced catalytic properties which are closely related to optimized electronic structure via compositional design are rarely in depth studied in LSBs.Simultaneously, the nano-alloy catalysts are lack of the chemical interaction with LiPSs through Li-non-metal bonds, and could not adjusted by non-metal ions.In contrast, TMCs have been extensively studied in LSBs, including metal oxides, sulfides, nitrides, carbides, phosphide, selenides, metal-organic framework (MOFs) due to excellent chemisorption and catalytic effect.Qian revealed that Co-based compounds followed the order of CoP > Co 4 N > CoS 2 > Co 3 O 4 to accelerate the redox kinetics of LSBs.The essential reason is that the p-band center of CoP was upshifted obviously, reducing the energy gap between the d-band center of Co and the p-band center [29].Metal selenides exhibit similar crystal structure and polarity characteristics to sulfides, while much higher conductivity and catalytic activity [30].All the metal-based catalysts contain d orbitals of transition metals that can be hybridized with the p orbital of S of LiPSs/Li 2 S, thereby reducing the reaction barrier by changing the electronic structure of LiPSs/Li 2 S [31,32].Moreover, the d and p orbitals of TMCs are hybridized with the p and s orbitals of S and Li in LiPSs, forming metal-S bonds and Li-nonmetallic bonds, which makes TMCs possess larger modulation space of electronic structure to anchor and catalyze LiPSs more effectively through introducing metal ions or anions [33,34].
Most importantly, it is difficult for single-component catalysts with single electron donor or acceptor nature to catalyze multi-step conversions of sulfur cathodes, and different metal cations of TMCs can provide different binding strength, binding preferences and catalytic functions for diverse LiPSs.It is of great significance to construct TMCs catalyst with more components for addressing the complex redox of LSBs through enriching active sites, designing multi-function and synergy effect [23,35,36].Additionally, TMCs catalysts with multiple metals/anions can optimize intrinsic catalytic activity with tuned electronic structure, and show huge room for regulation.Consequently, more and more TMCs catalysts with multiple metal ions or anions are proposed to enrich active sites, improve conductivity, chemisorption and catalytic activity.The design principles, structures and properties of various bimetallic compounds used as sulfur host materials, doping modification for carbon materials, C 3 N 4 and MXenes, and advances in heterostructure optimization for sulfur cathodes, interlayers and lithium anodes have been reviewed [37][38][39].However, the ways of introducing more cations/anions to modify TMCs, and the promoted mechanism have not been reviewed.Therefore, engineering strategies of TMCs to boost their catalytic effect as the focus are reviewed, and the unsolved problems as well as the further research is also prospected.

Engineering TMCs Catalysts
TMCs nanomaterials involve electronic interactions between metal ions and anions, and the electron density will be redistributed after the metal is coordinated with the anion, thus giving TMCs materials adjustable catalytic activity.Regulating the d-p orbital hybridization state of TMCs catalysts and LiPSs/Li 2 S by changing the electron structure of TMCs, is the essence to improve the catalytic activity.Engineering TMCs catalysts with multiple cations/anions can optimize intrinsic catalytic activity with tuned electronic structure through doping modification, constructing dual-ionic TMCs and TMCs-based heterostructure composites (Fig. 1a).These modification will enable TMCs catalysts with the superiority of enhanced catalytic activity, higher binding energies, more active sites, etc. (Fig. 1b).

Doping Modification
Heteroatom doping can not only enhance the electrical conductivity of TMCs, afford more chemical anchoring sites and higher adsorption energies for LiPSs, but also improve the charge transfer compared with undoped ones [40,41].The catalytic activity is thus enhanced, improving the sulfur utilization and electrochemical performance.According to the types of doped ions, doping modification includes cation doping, anion doping and dual doping.

Cation Single-Doping Modification
Since cations usually act as active sites, adjusting their electron structure is essential to improve catalytic activity [42].For example, surface defect was introduced into MoS 2 to enrich active sites by Ni doping, which promoted Li + / e − transfer, chemisorption and catalytic effect of Ni-doped MoS 2 toward LiPSs, improving the redox kinetics of LSBs.This rendered the sulfur cathodes with Ni-MoS 2 achieve a higher specific capacity of 1343.6 mAh g −1 with retained capacity of 800 mAh g −1 at 0.2C for 100 cycles than that of undoped MoS 2 (1287.8mAh g −1 , 678.3 mAh g −1 ) [43].Min found that the lattice spacing of Ni 0.2 Mo 0.8 N was larger than that of Ni 3 N and Mo 2 N due to the changed d-band position, improving the delocalization of electrons and lithium ions transfer.Additionally, because the Mo was more positive at the corners than Ni (Fig. 2a), Mo was partially etched by LiPSs during cycling, which generated much vacancies around Ni, accelerating charge transfer and LiPSs conversion.Furthermore, a built-in electric field was formed between the Ni 0.2 Mo 0.8 N modified separator and lithium metal due to the higher surface potential of Ni 0.2 Mo 0.8 N, which was beneficial for preventing the LiPSs diffusion and promoting Li + transmission [44].Co was also doped into MoS 2 , rendering the 2H MoS 2 transform into 1 T phase with sulfur vacancies, as illustrated in Fig. 2b.And it was easy for Co-doped MoS 2 to stabilize the 1 T phase and sulfur vacancies due to their lower formation energy of sulfur vacancies with 1.92 eV than MoS 2 (3.38 eV) (Fig. 2c, d).The electron-rich Co provided electrons for S and promoted the electron transfer, thus effectively boosting the adsorption capacity and catalytic activity, and  2e, f).Besides, the 1 T phase of Co-MoS 2 was increased accompanied by the decrease in sulfur defect when the Co content increased, further improving the adsorption and the electron transfer for LiPSs conversion [45].Cation doping can facilitate the reaction kinetic for both discharge process and charge process.Benefitting from the enhanced catalytic effect, Co-doped SnS 2 could promote the conversion of LiPSs to Li 2 S and reverse oxidation of Li 2 S.This was amply demonstrated by the obvious difference of S K-edge XANES, in which the feature of S-S disappeared during discharging from 2.0 to 1.7 V and re-appeared during charging process for S/ NCNT@Co-SnS 2 [46].Doping modification may introduce lattice distortion, which can enrich the active sites and regulate the electron structure to enhance the catalytic activity.Xu-doped CoTe 2 with Zn (Co 0.9 Zn 0.1 Te 2 ) and introduced lattice strain, which changed the coordination environment of Co atoms and further reduced the d-band center.Because the adsorption strength is related to the d-band center, and too strong adsorption is not conducive to the further conversion of LiPSs, the decline of d-band center of Co 0.9 Zn 0.1 Te 2 compared to CoTe 2 meant more electrons occupied in the antibonding orbitals, which was conducive to the desorption of LiPSs to preserve its effective catalytic active site.Furthermore, the charge number of Te atom near Zn atom was also increased, which enhanced the affinity between Te and Li, improving the anchoring capacity for LiPSs.As shown in Fig. 2g, h, the lattice strain enhanced the intrinsic catalytic activity, promoting the break of bonds of LiPSs/Li 2 S, thus reducing the energy barrier of Li 2 S 4 → Li 2 S 2 → Li 2 S from 2.05 and 1.94 eV for CoTe 2 to 0.51 and 1.6 eV for Co 0.9 Zn 0.1 Te 2 [47].Chen dissolved V into TiN lattice and formed solid solution Ti-V-N (TVN) in which V acted as dopant.As a result, Ti-N bonds were shorted while V-N bonds were lengthened, and the lattice parameter of TVN was reduced for the smaller atomic radius of V.More importantly, the structural distortion led to the d-band center of Ti lower while that of V increased, rendering V more effective to adsorb and catalyze LiPSs conversion.The best regulation was achieved at the Ti/V ratio of 4 for the largest structural distortion and highest d-band center of V, endowing the corresponding LSB with a retained capacity of 1036.8 mAh g −1 and a high capacity retention of 97.7% at 0.2 A g −1 for 400 cycles [48].
Of course, the catalytic effect is also heavily affected by the type of doping ions.Selecting suitable doping ions is of great significance to optimize the catalytic performance by tuning electronic structures (Fig. 3a), especially the d-band due to its electronic interaction with LiPSs (Fig. 3b), which also closely relates to adsorption strength.Zhao et al. doped SnSe with kinds of transition metals Ti, V, Mn, Fe, Co, Ni, Cu, Zn, and proved that all the doping significantly improved the adsorption ability toward LiPSs/S 8 , and promoted LiPSs/ S 8 conversion based on Gibbs free energy results.However, not all doping could reduce the length of Sn-S bond formed between SnSe and LiPSs/S 8 , indicating different catalytic mechanisms [49].Wang studied the influence of the electron structure on adsorption ability and catalytic performance of SmMn 2 O 5 , which was doped with major-group metals Mg, Ga and transition metals V, Cr, Fe, Mo at Mn site.The results showed that the binding energy for Li 2 S 4 , which was controlled by charge transfer, electronegativity difference between doped metal and S as well as surface work function of catalysts, had a linear relationship with the overpotential of sulfur reduction.Additionally, doping with Mg and Ga upward shifted the d-band center, while doping with transition metal had little effect [50].Zhang incorporated metal ions (Mn 2+ , Fe 2+ , Co 2+ , Ni 2+ and Cu 2+ ) into ZnS to study the relationship of catalytic activity and adsorption ability.As a result, the catalytic ability showed a volcano-shaped trend from Mn to Cu-doped ZnS based on the peak current of CV of symmetric cells (Fig. 3c).The adsorption ability of doped ZnS exhibited a decreased trend from Mn to Cu with downshift of d-band centers (Fig. 3d), while a volcano plot of reaction rates of LiPSs dissociation and desorption steps was obtained (Fig. 3e).This was because that the catalytic activity increased with improved adsorption ability, while too strong adhesion of Li 2 S passivated catalysts (Fig. 3f).Consequently, the catalytic activity showed a volcanoshaped relationship with adsorption ability, and Co-doped ZnS with medium adsorption ability achieved the best catalytic effect [51].
The properties of doping ions that boost the catalytic activity of the materials have also been studied.For promoting LiPSs adsorption and electron exchange, Mn, Fe, Co, Ni with more d electron numbers than V were doped into VN to adjust the electronic structure of VN by enriching its d electrons.As a result, adsorption energy (5.86 eV for Li 2 S 4 ) and interface electrons transfer (0.32 e) between LiPSs and catalysts were enhanced as Co was doped into VN in contrast to undoped VN (3.52 eV), which was ascribed to the lower filling fraction and higher d-band center of V 3d-band compared with undoped VN.Moreover, the best cathode performance could be obtained by Co-doped VN with retained capacity of 447 mAh g −1 at 3C for 500 cycles, which was more stable than other doped samples [52].Regulating the electronic structure of VN with d electron-rich elements (Mn, Fe, Co, Ni) could indeed improve the LiPSs adsorption and redox reactions.However, the relationship between the number of d electrons and catalytic performance is not concluded.
The electron donating ability of dopant ions also plays a key role in improving catalytic activity [53].Li proposed Cu as electron donor to dope CoP/MXene and control the redox kinetics of Li 2 S by regulating its electron structure and enriching active sites.To be specific, the doped Cu rendered the Co atoms charge accumulation, introducing unbalanced charge distribution and forming more Co/Cu-S bonds, which eventually increased the binding energy from 2.43 to 5.58 eV (Cu 0.1 Co 0.9 P), as shown in Fig. 2i.On the other hand, the strongly electronegative Co 3+ (15.26)  2.168 Å (Fig. 2j), while producing much lattice vacancy.As a result, the diffusion energy barrier and activation energy of nucleation/decomposition of Li 2 S were reduced (Fig. 2k), improving the redox kinetics of Li 2 S. With accelerated redox kinetics and enhanced sulfur utilization, the sulfur cathode with Cu 0.1 Co 0.9 P could achieve a specific capacity of 1475 mAh g −1 at 0.2C and a retention of 73.4% for 100 cycles, superior than that of CoP (57.6%) [54].
In addition, as the electronegativity affects the ability of TMCs to attract bonding electrons, the binding strength and electron transfer between TMCs and LiPSs are also affected [55].Therefore, electronegativity is also a key factor of doped ions to improve the catalytic performance.Hu-doped NiSe 2 with Fe with lower electronegativity than Ni and acted as electron donor to enhance the electron transfers from Fe-NiSe 2 to LiPSs.As a result, Fe-NiSe 2 improved chemisorption ability with the formed S-Fe and shortened S-Ni and Li-Se bonds between Fe-NiSe 2 and Li 2 S 6 .Additionally, Fe doping resulted in the increase in density of states (DOS) near the Fermi level and antibonding orbitals in conduction band, indicating improved electrical conductivity, which was conducive to catalyzing the redox of sulfur species [41].CoB  [51] Copyright: 2022, Springer Nature was doped with Mo with higher electronegativity than Co, forming a metal compound structure, and causing detachment of B and insertion/extraction of Li + to the vacancy during discharging and charging.Co 7 Mo 3 B was more prone to anchor long-chain LiPSs with higher binding energies and simultaneously conducive to the dissolution of Li 2 S 2 /Li 2 S with lower binging energy than CoB.As a result, the interaction of Co, B and Mo atoms could bidirectionally promote the redox kinetics [56].In addition, anti-selfdischarge behavior, ionic conductivity and Li + transportation could also be improved by doping modification, such as Ni-doped WS 2 [40].
The doping amount is also an important factor modifying catalysts.For example, when Fe doping content of TiO 2 increased from 1 to 5%, the capacity decay rate decreased from 0.27 to 0.08% at 1C for 500 cycles with accelerated kinetic reaction and decreased electrode polarization [57].Zhang et al. doped Fe into Co 3 O 4 and formed Co 3 O 4 hollow spheres with multi-shell structure and oxygen defects by adjusting the Fe doping amount.As a result, the electronic conductivity of Fe/Co 3 O 4 and the chemical adsorption for LiPSs were significantly improved, and catalytic sites were enriched, promoting the LiPSs conversion [58].
In addition to type and content of doping ions, doping site is also a key factor affecting the doping effect.Mn, Fe, Co, Ni etc. were selected to dope MoS 2 at Mo and S sites, respectively.Doping MoS 2 at Mo sites could not obviously enhance the binding strength for LiPSs.In contrast, doping at S sites improved the binding energies due to more electrons transferred from the adsorbed LiPSs to doped MoS 2 , which was ascribed to much stronger orbital overlap of Co-3d and S-3p of Li 2 S 4 taking Co-doped MoS 2 as an example.Furthermore, doped MoS 2 by substituting S exhibited good catalytic activity for LiPSs conversion with low Gibbs free energies [59].Doping site also has obvious influence on the band structure.Band structure of different types of Ti-doped SiO 2 were calculated, including substitutional type (Ti(S)-SiO 2 ) and impurities types which connected one O atom (Ti(I 1 )-SiO 2 ), two O (Ti(I 2 )-SiO 2 ) and O/Si (Ti(I 3 )-SiO 2 ).Their band gaps were 4.528, 2.468, 0.483 and 0.955 eV, respectively, which were smaller than that of pure SiO 2 (5.672 eV) [60].

Anion Single-Doping Modification
Anions doping can also promote the catalytic activity of TMCs with modified electronic structure, such as the d-band center and electron filling of metal ions.Firstly, anions doping can also enhance the electronic conductivity, such as S-doped Co 0.85 Se (1.05 eV) with lower band gap compared with that of Co 0.85 Se (1.07 eV).Moreover, the growth of Li 2 S could be regulated via the synergistic adsorption by Se and S [61].Anions doping can also enhance the chemical interaction with LiPSs.Wu-doped NiCo 2 S 4 with high amount of oxygen (37.28%) (Fig. 4a), obtaining NiCo 2 (O-S) 4 with lower conductivity (30.1 S cm −1 ) but superior trapping ability for LiPSs than natively oxidized NiCo 2 S 4 with O content of less than 10.0% (51.2 S cm −1 ).Specifically, Co was the dominated LiPSs interaction site of NiCo 2 O 4 and NiCo 2 (O-S) 4 , while that of NiCo 2 S 4 was Ni, which was proved by the intensity changes of Ni/Co XPS peaks before and after interacting with LiPSs (Fig. 4b).Electron transferred from the Li 2 S 6 to the O atoms, forming Li-O-M.As a result, NiCo 2 (O-S) 4 presented the best catalytic effect for promoting the LiPSs conversion than that of NiCo 2 O 4 with high charge transfer barrier due to poor conductivity and NiCo 2 S 4 for weaker interaction with LiPSs (Fig. 4c).As expected, the LSB of NiCo 2 (O-S) 4 achieved a preferable cycling stability compared with NiCo 2 O 4 and NiCo 2 S 4 , maintaining a capacity of 962 mAh g −1 after 200 cycles at 0.2C and 922 mAh g −1 after 150 cycles at 0.5C [62].
The properties of doped anions and promoted mechanism that enhance the catalytic activity of TMCs have also received attention.N with higher electronegativity than Se was selected to modify CoSe 2 , which could elongate S-S of LiPSs and Li-S bond of Li 2 S but shorten Co-S bond, resulting in facilitated conversion of sulfur species both in discharge and charge process.The enhanced chemisorption and catalytic capacity of N-CoSe 2 was due to less filled antibonding states and facilitated charge transfer with higher d-band center of Co compared to CoSe 2 (Fig. 4d).In addition, the charge number of Co atoms was increased to provide more empty orbitals for adsorbing LiPSs (Fig. 4e) [63].N doping could also tune the electron filling state of TMCs to regulate the adsorption ability as well as conversion kinetics for LiPSs.The electron density of Ta around N in N-Ta 2 O 5 was increased compared to Ta 2 O 5 , because fewer electrons in Ta d orbitals flowed into N than O for the relatively weak electron binding ability of N. As a result, d orbitals electron filling of Ta in N-Ta 2 O 5 (2.96) was higher than that of Ta 2 O 5 (2.87) but lower than that of Ta 3 N 5 (3.23), corresponding to the charge transfer amount between Ta of N-Ta 2 O 5 , Ta 2 O 5 , Ta 3 N 5 and S, which imparted N-Ta 2 O 5 (3.70 eV for Li 2 S 4 ) moderate ability to anchor LiPSs compared to that of Ta 2 O 5 (6.94 eV) and Ta 3 N 5 (2.82 eV).The sulfur cathode with N-Ta 2 O 5 exhibited the highest initial capacity of 1252.8 mAh g −1 and capacity retention rate of 92.7% at 0.2C for 100 cycles among the studies catalysts [64].
P with higher electronegativity than Te was also selected to dope NiTe 2 with Te vacancies.The P atoms occupied Te vacancies instead of taking the place of Te atoms (Fig. 4f).The higher electronegativity of P than that of Ni and Te rendered it attract nearby atoms and trigger bonds reconstruction, shortening the Ni-Te of P-NiTe 2-x .Additionally, the shortest S-Ni and Li-Te bonds between P-NiTe 2-x and LiPSs (Fig. 4g) demonstrates the strongest anchoring effect.And electron density of Ni-S was decreased while that of Li-Te was increased when P-NiTe 2−x interacted with Li 2 S (Fig. 4h), meaning a promoted catalytic activity [65].However, Hu et al. doped P with lower electronegativity than Se into NiSe 2 .As a result, the electron-rich P promoted the electrons transfer from Li 2 S 6 to P-NiSe 2 , and the S at the end of Li 2 S 6 showed apparent electron deletion, rendering it present superior catalytic effect than NiSe 2 [66].P was also used to dope MoS 2 and hybridized with Mo 3d and S 2p orbital, resulting in more charge transfer and superior conductivity.This induced stronger Mo-S and P-Li bonds and longer S-S/Li-S bonds of LiPSs/Li 2 S to accelerate their conversion [67].Similarly, CoS 2 doped with P with relatively low electronegativity also improved the catalytic activity [68].Therefore, whether the electronegativity of doping ions is the key factor to regulate the catalytic activity of TMCs, and their relationship as well as the promoted mechanism needs to be further studied.
The valence states of TMCs can also be optimized by doping to enhance catalytic activity.Chen's group modulated the valence states of Ni and Zn for Ni 3 ZnC 0.7 by P doping and accompanied Zn vacancies, which remarkably decreased the electron density at Zn sites to anchor LiPSs.Meanwhile, the content of Ni 2+ species was slightly increased to facilitate electron transfer between Ni 2+ /Ni(0) and LiPSs, improving the catalytic effect for LiPSs conversion.The LSB with P-doped Ni 3 ZnC 0.7 modified separator could present a more stable cycle performance with an initial capacity of 684 mAh g −1 and fading rate of 0.0247% at 1C for 1400 cycles, in contrast to that of pristine Ni 3 ZnC 0.7 with 583 mAh g −1 and 0.0341%, respectively [42].

Dual-Doping Modification
Due to the synergistic effect between doping ions, dual-doping modification could obtain better catalytic performance than single doping.Lee et al. designed Co and P dual-doped MoS 2 (Fig. 5a), in which Co doping changed MoS 2 phase from 2H to 1 T, improving its conductivity and providing more effective electron conduction (Fig. 5b).More importantly, the Co-P coordination formed after P doping further improved the catalytic activity of Mo 0.9 Co 0.1 S 2 .As a result, Co and P co-doping improved the catalytic performance for LiPSs conversion with lower energy barriers (Fig. 5c).Benefitting from the synergistic effect of Co and P dualdoping, P-Mo 0.9 Co 0.1 S 2 obtained the best cathode performance.Represented by the rate performance, P-Mo 0.9 Co 0.1 S 2 presented a high capacity of 931 mAh g −1 at 6C, in contrast to that of Mo 0.9 Co 0.1 S 2 with 633 mAh g −1 and MoS 2 with 338 mAh g −1 [69].Li et al. modified CoSe 2 with Ni and Zn dual-doping to bidirectionally catalyze the redox of sulfur cathodes.To be specific, the catalytic effect of Ni-doped CoSe 2 for the LiPSs conversion in the discharge process was better than that of Zn doping modification, while Zn doping achieved better catalytic performance on the Li 2 S decomposition.In addition, Ni/Zn dual-doping CoSe 2 had the better catalytic performance than that of the mixture of Ni-doped CoSe 2 and Zn-doped CoSe 2 [55].TMCs co-doped by anions was also involved.N, F, and B were co-doped into CoFe 2 O 4 and induced rich O vacancies to enhance the conductivity and act as adsorption, catalytic sites for LiPSs.The density functional theory (DFT) results also showed that new electron energy peaks appeared and increased the carrier density after the anions co-doping modification.Consequently, the improved binding energy and catalytic effect of modified CoFe 2 O 4 suppressed the shuttle effect and boosted the redox of sulfur cathodes, delivering an excellent electrochemical performance with maintained capacity of 1156 mAh g −1 at 0.2C for 300 cycles as separator coating layer, which exceeded that of pristine one with only 825 mAh g −1 [70].
Metal ion-doped metal compounds are usually prepared in two ways.The first is to directly add stoichiometric-doped metal salt during the hydrothermal reaction or co-precipitation reaction.For example, Ni-doped MoS 2 was prepared by hydrothermal treatment of the mixture of oxalic acid, thiourea, (NH 4 ) 6 Mo 7 O 24 •4H 2 O and Ni(Ac) 2 •4H 2 O, and the doping content could be controlled by amount of metal salts [43].The second is adding the metal salt of the doping ions to some solvent along with the pristine metal compound or its precursor, and further replace the metal ions in the metal compound for doping through heating or hydrothermal conditions.Taking doped SiO 2 as an example, M-SiO 2 (M = Ti, Al, Sn) were synthesized by hydrothermal treating the mixture of SiO 2 and stoichiometric metal source in isopropyl alcohol [60].As for anion doping of TMCs, metal compounds and chemical reagents containing doping sources are usually calcined at high temperatures, such as ammonium hydrogen carbonate, sodium hypophosphite and sodium hydrogen sulfite as a nitrogen source, phosphorus source and sulfur source, respectively.For example, N-doped CoSe 2 was synthesized by calcining the CoSe 2 accompanied with ammonium hydrogen carbonate [63].Furthermore, anion and cation co-doping can be carried out by single doping of metal ion and then anion doping.
Although reasonably engineering TMCs catalysts could promote the LiPSs conversion, the design and regulation of ideal bidirectional sulfur catalyst is still a great challenge for the difficulty of selecting ions with different functions [71].Different doping ions in TMCs may play various functions, such as improving conductivity, regulating electronic structure, and adsorbing-catalyzing different LiPSs in different stages of LSBs.Moreover, multicomponent co-doping may enrich the active sites and play a synergistically catalytic role [72].However, research on this aspect is lacking, and it is worth further study, especially the selection and matching of multi-doped ions and their synergistic catalysis mechanism through deeply studying the regulation rules of electronic structure.Based on this development, high-entropy doping may be proposed.Additionally, it is found that the external magnetic field could regulate the spin polarization of CoS x catalyst, drive the transition of Co 3+ electrons from the low spin state to the high spin state, generating additional unpaired electrons in the 3d orbit of Co and enhancing the hybridization between Co-3d and S-2p orbital.As a result, the charge transfer dynamics at the CoS x /LiPSs interface was promoted, and the adsorption-catalytic capacity for LiPSs was significantly improved [73].Doping is also an effective strategy to manipulate spin polarization of catalysts to enhance the catalytic activity [74,75].Therefore, the adjustment of spin effect induced by doping should be paid enough attention in LSBs.In addition, doping modification may introduce defects such as vacancy in TMCs, which may provide additional adsorption and activation sites [76].It is worth noting that doping may cause changes in d-band center, spin polarization, lattice distortion and vacancy defects at the same time.Therefore, controlling electronic structure through doping is complicated and these factors should be comprehensively investigated.Furthermore, directed doping to specific sites should be developed for higher catalytic activity [77].

Multi-Ionic TMCs
Multi-ionic TMCs composed of more metal ions or anions also possess enriched active sites, optimized chemical properties, and improved catalytic activity compared with TMCs of one component.In contrast to doping modification which belongs to a kind of defect and retain the phase and crystal structure of the original TMCs, bimetal TMCs with fixed atomic ratios within a certain range are solid solutions and possess unique crystal structures, such as Co 3 Mo 3 N, BaTiO 3 and FeWO 4 , and only some may be identical to one-component TMCs, such as Ni 2 Co 4 P 3 .Furthermore, doping modification can be achieved by introducing heterogeneous ions, but the synthesis methods cannot be simply transplanted to the preparation of dual-ionic metal compounds.Multi-ionic TMCs are usually not obtained by increasing the content of doped ions in TMCs.Increasing the doping amount may lead to changes in crystal phase besides changed lattice parameter and reconstructed bonds, and even anion aggregation and phase collapse [78,79].

Bimetallic TMCs
Compared with corresponding single-component compounds, bimetallic TMCs can achieve better conductivity and electrochemical activity, which have also been applied to catalyze LiPSs conversion.Zhang synthesized NiCo 2 S 4 microspheres, which possessed good electrical conductivity and catalytic activity, ensuring fast conversion kinetics of LiPSs [80].Ni-Co phosphide nanoparticles embedded in carbon hollow nanocages were also designed as adsorption-catalytic sites, promoting redox reaction and Li + diffusion in LSBs [81].The reasons why bimetallic TMCs are superior to monometallic TMCs have also been studied.NiCoP possessed a significantly higher binding energy of 4.24 eV for LiPSs than CoP (1.48 eV), because the natural oxidation of NiCoP formed Ni-O-P and Co-O-P and activated the Co/Ni sites, rendering it bind with LiPSs through Co-S and Ni-S bonds [82].In addition, bimetallic TMCs can also establish more suitable chemical bonds to optimize chemisorption effect.For example, TiO 2 anchored LiPSs with S-O bonds, while bimetal Li 4 Ti 5 O 12 could form more efficient Ti-S bonds (Fig. 6a), resulting in excellent cyclic stability of sulfur cathode at sulfur loading of 4 mg cm −2 with 80% capacity retention at 1C for 300 cycles [83].Na 2 Ti 6 O 13 with synergistic coordination of Na and Ti provided double-cations as adsorption sites for promoting LiPSs conversion and preventing their accumulation (Fig. 6b).Furthermore, the distortion of TiO 6 octahedron in Na 2 Ti 6 O 13 generated a large dipole moment, and the internal polarization field in TiO 6 octahedron was favorable for electron transfer, promoting the conversion of LiPSs and significantly enhancing the adsorption ability compared with TiO 2 .The LSB with Na 2 Ti 6 O 13 could reach a capacity of 815 mAh g −1 at 1C and maintained its capacity at 84% at 0.1C for 100 cycles compared with that of TiO 2 at 75% [84].Additionally, the conductivity and charge transport could also be improved compared to the monometallic compounds [85].
The fundamental reasons for elevated adsorption and catalytic ability of bimetallic TMCs are further explored.Electron transfer between different metals of bimetallic TMCs can tune the electronic structure such as distribution of electron density, thus adjusting the adsorption and catalytic properties [86].Zhang designed Co 3 Mo 3 N by calcinating Mo-doped ZIF-67, and the electron redistribution was occurred with the introduction of Mo due to its greater electronegativity than Co.As a result, electron transferred from Co and Mo to N atoms, and the electron density around Co was decreased while that of N was increased, facilitating the adsorption and conversion of LiPSs [20,87].
In addition, tuned valence state is also an important reason for enhanced catalytic capacity of bimetallic TMCs.For example, electron transfer was occurred from Co to Sn in CoSn(OH) 6 due to their different electronegativity, which increased the Co 3+ and decreased the valence state of Sn compared with Co(OH) 2 and Sn(OH) 4 .As a result, the chemical interaction between Co and S were enhanced, while that of Sn and S was weakened for CoSn(OH) 6 after discharge-charge, presenting a moderate adsorption capacity, which promoted the LiPSs diffusion for conversion [86].Chemical valence could also be varied after interaction with S/LiPSs to boost the redox of sulfur species.Co 3+ and Ni 3+ were in situ formed attributed to the interaction between nickel-cobalt double hydroxide (NiCo-DH) and sulfur, which was conducive to the oxidation of initially formed LiPSs and the formation of thiosulfates.The reversible redox between thiosulfates and LiPSs could confine LiPSs and catalyze their conversion.Moreover, NiCo-DH underwent a redox with Li 2 S 6 , partially reducing Co 3+ and Ni 3+ to Co 2+ and Ni 2+ .The electron transfer and strong coupling effects between Ni and Co in NiCo-DH rendered it a smaller redox potential [88].Li x MoO y was in situ synthesized by electrochemically activating MoO 3 at about 2.6 V, which subjected to a conversion between Li 0.042 MoO 3 and Li 2 MoO 4 at about 2.2 V, thus accelerating the redox of LiPSs with the potential overlap [89].
Interaction between metal sites can also regulate the d-band electron filling and d-band center, thus improving chemisorption and catalytic property for LiPSs.Zhang alloyed Co to Ni 2 P to improve the d-band of Ni 2 Co 4 P 3 (Fig. 6c), in which the Co 3d-band in Ni 2 Co 4 P 3 was higher than the Ni 3d-band in Ni 2 Co 4 P 3 and Ni 2 P. Because Co 3d had lower electron fill number and higher d-band center than Ni 3d (Fig. 6e), Ni 2 Co 4 P 3 was endowed with enhanced interaction with LiPSs and reduced activation energy for LiPSs conversion (Fig. 6d).Additionally, Ni 2 Co 4 P 3 formed a shorter metal-S bond with LiPSs and weakened S-S bonds of LiPSs, reducing the energy consumption of S-S bonds and energy barrier for conversion reaction compared with Ni 2 P. The crystal orbital overlap population of S-S bond (2024) 16:97 Page 13 of 33 97 1 3 at both ends showed that the electron filling of antibonding state of Li 2 S 4 on Ni 2 Co 4 P 3 was higher than Ni 2 P (Fig. 6f) [90].
For host materials with relatively low conductivity but strong interaction with LiPSs, such as metal oxides, the surface diffusion of LiPSs/Li 2 S is vital for electrochemical reactions [19].Fortunately, bimetallic TMCs can also promote the diffusion of Li 2 S. For example, BaTiO 3 delivered a much lower diffusion energy barrier of Li 2 S than TiO 2 , showing superior surface diffusion kinetics and more uniform dispersion of Li 2 S.More importantly, BaTiO 3 with inherent self-polarization showed promoted redox kinetics of LiPSs/ Li 2 S than TiO 2 (Fig. 9g).As a result, the LSB equipped with BaTiO 3 could deliver an initial capacity of 896 mAh g −1 with remained capacity of 466.1 mAh g −1 at 1C for 1000 cycles, exceeding that of TiO 2 with retained capacity of 210 mAh g −1 [91].Similarly, Bi 4 Ti 3 O 12 with inner electric field induced by spontaneous polarization showed excellent catalytic activity for promoting LiPSs conversion [92].The intermolecular polarization of CoIn 2 S 4 and Li 2 S 4 introduced by their strong interaction was regarded as an essential reason of reduced conversion barrier and enhanced charge transfer from CoIn 2 S 4 to Li 2 S 4 [93].Additionally, Li + diffusion can also be promoted.Compared to Ni 3 C, Ni 3 ZnC 0.7 could provide Ni, Zn sites as sulfiphilic sites and lithiophilic sites, respectively, which reduced energy barriers of Li + diffusion and improved catalytic property [94].
Bimetallic TMCs may also combine the advantages of the two metal ions or corresponding monometallic TMCs.Liu designed Co 3 V 2 O 8 to make use of V, Co binary active sites to anchor LiPSs and catalyze their conversion [95].FeWO 4 nanorods was designed for combining the merit of Fe 2 O 3 with strong affinity and WO 3 with good catalytic property, delivering a faster Li + diffusion rate, stronger chemical binding and better redox kinetics for LiPSs.Thanks to the simultaneous satisfaction of adsorption and catalysis, Li 2 S 6 cathode with FeWO 4 obtained more stable cycling properties with retained capacity of 519 mAh g −1 at current of 3.2 mA after 600 cycles than that of Fe 2 O 3 only with 502 mAh g −1 after 150 cycles [96].For MoWS catalyst, 1 T phase structure with better electron conductivity possessed higher catalytic activity, while 2H phase was beneficial for Li + diffusion [87].Mo 0.5 W 0.5 S 2 composed of 2H-1 T mixed phase, possessed both superior catalytic activity for LiPSs conversion and a faster electron transport, delivering a better reaction kinetic than that of MoS 2 and WS 2 [97].Bidirectional catalysts can also be constructed with bimetallic TMCs.For example, Shu introduced Mo into NiO and constructed NiMoO 4 with increased electron density, which led to the decrease in bandgap from 2.51 eV (NiO) to 0.56 eV (NiMoO 4 ) and the improvement of metallic properties.Furthermore, NiMoO 4 rendered the S-S bonds and Li-S bonds of adsorbed Li 2 S 4 and Li 2 S longer, and Gibbs free energy of the rate-determining step (Li 2 S 2 → Li 2 S) and Li 2 S decomposition barrier for NiMoO 4 (0.90 eV, 0.19 eV) reduced compared with NiO (1.15 eV, 1.73 eV), simultaneously facilitating the conversion of LiPSs and Li 2 S oxidation (Fig. 6h) [98].
Introducing metal ions may also affect the morphological structure to help optimize the cathode performance.Zhang prepared NiCo hydroxide polyhedrons by etching ZIF-67 with Ni(NO 3 ) 2 •6H 2 O because of its lower pH than Co(NO 3 ) 2 •6H 2 O in ethanol.The obtained NiCo hydroxide with denser and miniaturized nanosheets along the polyhedral shells, facilitated the exposure of enriched active surfaces for chemical anchoring LiPSs and catalyzing their reactions.Consequently, bimetallic NiCo hydroxide hollow polyhedra was more conducive to improving the electrochemical performance of LSBs, endowing the corresponding sulfur cathode with a higher capacity of 763 mAh g −1 after 100 cycles at 0.1C than that of Co hydroxide of only 406 mAh g −1 [99].
MOFs with the merits of tunable pore structures, structural diversity as well as functional versatility, are extremely suitable for chemical anchoring and physical confining LiPSs with Lewis acid-base interaction and porous structure, and catalyzing the LiPSs conversion [100,101].Furthermore, bimetallic MOFs can improve its electronic conductivity, enrich active sites, and plays synergistic effects.For example, considering that Al 3+ in Al-MOF was coordinatively saturated and hardly to bind extra LiPSs, coordinatively unsaturated Cu 2+ with sulfiphilicity was introduced to construct bimetallic Al/Cu-MOF, which generated additional sites for anchoring LiPSs and enhanced the interaction [102].A Zr-Fc MOF possessed positively charged Zr sites provided by uncoordinated Zr-O defects and positively charged oxidized Fc + , to electrostatically adsorb LiPSs.At the same time, acidic protons in the defect sites of Zr-O nodes could also anchor LiPSs.These abundant anchor sites and electrocatalytic activity of Zr-Fc MOF enabled the LSBs a superior cycle stability compared to Zr-MOFs [103].
To catalyze multi-step redox process, catalyst with two kinds of catalytic sites were proposed.NiCo-MOF was thus designed by combining the different catalytic function of Ni-MOF and Co-MOF.As shown in Fig. 7a-c, Ni-MOF preferred to bind the long LiPSs and delivered lower Gibbs free energy for their conversion, while Co-MOF anchored the short LiPSs stronger, facilitated their reduction and Li 2 S oxidation.Furthermore, NiCo-MOF possessed better conductivity (Fig. 7d) and improved catalytic activity, because charge redistributed between Ni and Co (Fig. 7e, f) for their asymmetric interaction with the bridge O, and led to the change of the unfilled metal electron orbitals [104].Wang also designed NiCo-MOF and the charge transfer from Co to Ni due to the higher electronegativity of Ni 2+ than Co 2+ , which rendered electron density increase in the Ni center.NiCo-MOF achieved the best adsorption effect and catalytic capacity for LiPSs conversion as a result of synergistic effect.To be specific, the Ni-MOF showed the better catalytic effect on LiPSs conversion than Co-MOF, while Co-MOF exhibited a stronger interaction with LiPSs than Ni-MOF [105].To realize effective adsorption and catalysis, Mai adjusted the metal sites by constructing bimetallic Zn/Co-ZIF (Fig. 7g).Specifically, Co site delivered better catalytic activity and Zn site could anchor LiPSs more strongly.By adjusting the Zn:Co ratio and using the Zn/ Co-ZIF with a mole ratio of 0.9 as a separator modification layer, optimized cycling and rate performance of LSBs could be achieved.Its initial capacity was 1304 mAh g −1 and could maintain at 1141 mAh g −1 after 100 cycles [12].The interaction between bimetallic MOFs and sulfur species can be optimized by adjusting the types of incorporated metal ions and tuning the electronic structure of metal sites with changed coordination environment.For example, a series of bimetallic MnM-MIL-100 (M = Co 2+ , Ni 2+ , Zn 2+ , Pb 2+ and etc.) were synthesized, in which Co could modify the electronic structure of Mn, and the decrease in Ni content changed the electronic environment of Ni 2+ [106].

Medium/High-Entropy TMCs
TMCs with more than two kinds of metal cations are also designed for LSBs.For example, Cu 2 ZnSnS 4 with Cu, Zn and Sn as active sites was prepared to adsorb LiPSs and promote the redox reaction [107].Considering the combination of various advantages of different TMCs and the cooperating effect of multi-metals, high-entropy materials (high-entropy alloys and high-entropy ceramics) containing more than five kinds of metal elements are also applied in LSBs.High-entropy materials with a single-phase crystal, possess significant advantages of lattice distortion and 'cocktail' effect, presenting a distinguished synergistic effect and incomparable catalytic activity [108].Considering that Co-doped ZnS, CoS, and Cu-based materials are known catalytic materials for LSBs, Abruna combined Zn, Co, and Cu with In, Ga into the sulfide material to balance the charge, and designed high-entropy sulfide Zn 0.30 Co 0.31 Cu 0.19 In 0.13 Ga 0.06 S to facilitate the redox kinetic and alleviate the shuttle effect of LSBs.As a result, the high-entropy sulfide exhibited superior catalytic properties than any constituent metal sulfides in both discharge and charge stages.It was noteworthy that although GuGaS 2 and CuInS 2 had catalyzed the reduction reaction, no metal sulfides catalyzed the oxidation reaction, and the high-entropy sulfide showed significantly improved oxidation kinetics due to the synergistic interaction between the components of the high-entropy sulfide [109].Qiao designed high-entropy oxide composed of highly dispersive Ni, Mg, Cu, Zn and Co, which exposed abundant active sites, and could strong anchor LiPSs with Li-O and S-Ni bonds and catalyze LiPSs conversion of (Fig. 6i) [110].High-entropy metal nitride of V, Cr, Nb, Mo and Zr was also applied as sulfur host.The electron transferred from S x 2− (4 ≤ x ≤ 8) to high-entropy metal nitride, and the XPS peaks of X 3+ -N bond (X = Nb, Mo, Cr, V, and Zr) all shifted to lower binding energies with similar shift value, meaning the homogeneity and equality of those metals [111].The (Mg 0.2 Mn 0.2 Co 0.2 Ni 0.2 Zn 0.2 )Fe 2 O 4 nanofiber could provide large number of active sites for adsorbing LiPSs and synergistically promoting LiPSs conversion, Li 2 S deposition and  [112].
In addition, more than two kinds of metal ions can also be introduced into MOF materials to further enrich their active sites, improving their electrochemical properties.Pang designed FeCoNi prussian blue analogs (PBA), in which Fe, Co, and Ni could all act as binding sites for Li 2 S 4 (Fig. 7h), achieving highest adsorption energy than that of FeCo-PBA and FeNi-PBA [113].Furthermore, Pang constructed PBA ranging from binary to high entropy to explore the effects of different metal on the coordination environment, the mechanism of LiPSs conversion and the cathode performance.As a result, Fe coordinated with C, while Co, Ni, Cu, Mn and Zn all participated in N coordination.More importantly, high-entropy PBA delivered faster Li + diffusion, minimum charge transfer resistance and faster LiPSs conversion, promoting the corresponding LSB to achieve the best cycle performance with an initial capacity of 1335.6 mAh g −1 and residual capacity of 570.9 mAh g −1 after 200 cycles at 0.1C, which was better than the LSBs with NiFe-PBA (1129.0mAh g −1 , 339.5 mAh g −1 ), NiCuFe (1169.1 mAh g −1 , 389.8 mAh g −1 ), and CoNiCuFe (1218.3mAh g −1 , 467.0 mAh g −1 ) [114].
All in all, the study of high-entropy materials for LSBs is still in its infancy.Although high-entropy materials show better catalytic performance than their constituent components, the functions of each component, the synergies between each component and the mechanism of how to play the catalytic role are worthy of more in-depth discussion, which is conducive to the selection and matching of components of high-entropy materials to design efficiently multi-functional sulfur catalysts.For example, high-entropy alloy FeCoNiMnZn as catalyst had been shown to simultaneously improve the reaction kinetic for both in discharge and charge process of LSBs.This could be ascribed to the optimized electronic structure, that is, the d-band center of FeCoNiMnZn moved upward than that of FeCoNi and Zn, thereby increasing the adsorption energy and electrons transfer toward LiPSs.The electron density differences combined with partial projected density of states (PDOS) further displayed that Zn acted as an electron reservoir, Mn dominated the conduction band and promoted electron consumption, and other elements played the role in regulating charge distribution [115].In addition, the chemical and structural stability of high-entropy materials in the charging and discharging process of LSBs should be considered.It was found that the copper in Zn 0.30 Co 0.31 Cu 0.19 In 0.13 Ga 0.06 S was leached out as an ionic species, accompanied with the smaller particles and lower crystallinity of high-entropy sulfide, gives a good indication that stabilizing cations could prolong the life of catalysts and improve the capacity retention ability [109].Furthermore, the significant lattice distortion is also one of the key factors for the excellent catalytic performance of high-entropy materials.Nevertheless, how to control the lattice distortion of high-entropy materials and the relationship between it and catalytic activity has not been studied.Additionally, more high-entropy TMCs should be designed, such as high-entropy fluorides, high-entropy chlorides [116,117].
Moreover, given that the composition range of highentropy alloys is very large (1050 possible alloy components based on elements commonly used in the periodic table) and the traditional trial-and-error approach is too cumbersome for the design of high-entropy materials, high-throughput theoretical calculations combined with machine learning is an effective approach and has been widely used in the composition design and optimization of high-entropy catalyst in recent years [118,119].For example, using DFT calculations, Singh considered more than 1280 adsorption sites on the designed FeCoNiCuMo catalyst, developed three machine learning models to predict the adsorption of some important intermediates in the CO 2 reduction process, and further analyzed the structure-performance relationship of catalysts to CO 2 reduction [120].Guo's group proposed a first principles computational theory method for machine learning-aided design to study the oxygen reduction reactivity of millions of reaction sites on the surface of six kinds of high-entropy alloys, accurately predicting the catalytic activity of millions of reaction sites [121].Luo and Chen revealed the atomic distribution, surface atomic structure and local coordination environment of high-entropy alloys based on machine learning, and further revealed the origin of highly efficient alkaline hydrogen oxidation reaction properties of high-entropy alloys combined with the DFT calculation [122].Unfortunately, the research of highthroughput technology combined with machine learning has been rarely reported in the field of LSBs, which may be the future research hotspot of high-entropy materials applied to LSBs, due to the adsorption and catalytic mechanisms that can be used for reference.

Bi-anionic TMCs
Just like the implant of metal ions, TMCs with suitable dual-anions will also improve the conductivity and electrochemical activity [123].Most importantly, the adsorption for LiPSs and the catalytic effect can also be well regulated by modifying the anions [29].Zhou introduced Se into MoS 2 lattice by anion substitution, which led to many anion vacancies and an increase in interlayer spacing due to the difference of radius and electronegativity of Se and S atoms (Fig. 8a).MoSSe delivered much higher binding energies (Fig. 8b) with sulfur species than MoS 2 and MoSe 2 and possessed higher conductivity with lowest bandgap (Fig. 8c).Furthermore, experiment results also demonstrated accelerated redox kinetics and alleviated LiPSs shuttle, as well as great lithiophilicity for lithium electrodeposition (Fig. 8d,  e).As a result, MoSSe could simultaneously accommodate sulfur and lithium (Fig. 8f), and the corresponding full cell could achieve a discharge capacity of 637.3 mAh g −1 at 1C for 1000 cycles and stable cycle (Fig. 8g) [124].The high binding energy of Li better adsorption effect for LiPSs and promoted LiPSs conversion with a higher conversion free energy compared to CeO 2 [126].
BiOX (X = Cl, Br and I) with Bi located at outer surface of the molecular and X with larger electronegativity at inter, provided vacant orbitals of Bi as active sites and accepted electrons from LiPSs, showing excellent ability to adsorb LiPSs and catalyze their conversion [127].Among them, BiOI was more suitable for its good conductivity with a smaller bandgap (1.9 eV) compared to BiOBr (2.9 eV) and https://doi.org/10.1007/s40820-023-01299-9© The authors BiOCl (3.5 eV).Furthermore, BiOI achieved better ability to capture LiPSs and bidirectionally promote their conversion.This could be proved by higher binding energies, smallest Tafel slope, larger nucleation capacity of Li 2 S, highest current and smallest polarization displayed in Li 2 S 6 symmetrical cells compared with the others [128].
Because too strong interaction between Ti 3 C 2 and S 8 / LiPSs caused the decomposition of sulfur species, Ti 3 C 2 must be modified with surface terminating groups.Therefore, functionalized Ti 3 C 2 T 2 (T = N/O/S/F/Cl) with d-p hybridization between Ti and T were studied as sulfur host.The binding energies were in the sequence of Cl < F < N < O < S, and the kinetic evaluation and Li + diffusion got worse in the order of Ti which were closely associated with their interactions with sulfur species [129].Compared with Ti 2 NO 2 (2.07 eV taking Li 2 S as an example), Ti 2 NS 2 (3.42 eV) possessed larger adsorption energies with sulfur species, which mainly provided by the interaction between Li atoms of LiPSs and S atoms of Ti 2 NS 2 .In addition, the Ti 2 NS 2 exhibited metallicity that derived from the d orbital of Ti and the p orbital of S, and could maintain a high conductivity even after adsorbing LiPSs to facilitate the electrochemical reactions [18].
Hydroxyl oxides, a kind of compounds made up of oxygen ions, hydroxide ions and a metal ion, has also been applied in LSBs.Hydroxy iron oxides (FeOOH) with Fe-O, Fe-OH bonds and good conductivity were used to accommodate sulfur, in which transition metal and hydroxyl acted as adsorption sites for LiPSs and accelerated electron transfer between the catalyst and LiPSs, exhibiting good effect for capturing and catalyzing LiPSs [130,131].Similarly, MnOOH with Lewis acid sites Mn 3+ cation could anchor LiPSs by forming Mn-S bond [132].Moreover, the TMCs with dual-cations and dual-anions were designed.For example, LiVPO 4 F was applied to boost the kinetic of sulfur species, which provided both p orbitals and d orbitals of O, V, F, P atoms to interact with LiPSs [133].
In conclusion, compared to TMCs with single cation/ anion, dual-ionic TMCs possess higher conductivity, better chemisorption effect and multiple active sites for catalyzing LiPSs conversion.However, the dual-ionic TMCs still lack in design basis, especially for the bidirectional catalysts.Additionally, there is a lack of research on the optimization of catalytic sites and catalytic activity by regulating the band structure, valence state, electron density of dual-ionic TMCs by adjusting the ions type, content, electronegativity, and ion radius difference.It is worth noting that the d-band center, spin polarization, and other electronic structures of dual-ionic TMCs can also be regulated by changing ion species, which is worthy of further exploration.Furthermore, although doped ions may not be able to form dual-ionic TMCs, and doping and dual-ionic TMCs are similar ways of modifying TMCs by introducing heterogeneous ions, the modification effects and mechanisms of the two should be compared, possibly by regulating the content of introduced heterogeneous ions.Furthermore, high-entropy materials with multi-anions are also of great interest but have not been widely studied [116].Additionally, more modification methods should also be introduced to further improve dual-ionic TMCs, such as bimetallic TMCs quantum dots [134].Bimetallic TMCs can also be combined with doping modification strategy to construct multi-functional sulfur hosts, such as N-doped CuCo 2 O 4 [135].

TMCs-Based Heterostructure Composites
When a kind of TMCs cannot simultaneously meet the needs of chemical binding with LiPSs and catalyzing their transformation, the heterostructure composites of two kinds of TMCs can be constructed with complementary advantages.For example, MoSe 2 has excellent electrical conductivity and catalytic performance, but lacks sufficient chemisorption for LiPSs, while MoO 2 has superior chemical binding effect.Therefore, the synergistic effect of efficient capture and catalytic transformation for LiPSs could be achieved with MoSe 2 /MoO 2 heterostructure [136].The edge sites of MoS 2 possess high catalytic activity, while the basal planes have little activity.Zhang et al. grew CoSe 2 on the base surface of MoS 2 to form heterostructure, synergistically utilizing the superior chemisorption capacity of CoSe 2 and the excellent catalytic activity of MoS 2 edge sites (Fig. 9a).The CoSe 2 / MoS 2 interface also had higher binding energy with LiPSs than CoSe 2 and MoS 2 , which was confirmed by much more accumulated electrons at adsorption regions (Fig. 9b).As a result, compared to CoSe 2 and MoS 2 , the LSB equipped with CoSe 2 /MoS 2 delivered a most stable cycle performance with initial capacity of 825.5 mAh g −1 at 2C and retained capacity of 714.5 mAh g −1 after 600 cycles [137].Similarly, Zhao et al. constructed Ni/Ni 2 P heterostructure to combine the strong adsorption of Ni 2 P for LiPSs and catalytic activity of Ni [138].A kind of heterostructure composed of 0D bimetallic CoZn-Se nanoparticles on 2D nitrogen-doped MXene was designed, providing double lithiophilic-sulfiphilic binding sites through forming Co-S, Li-Se, Ti-S and Li-N/ Li-O bonds to adsorb LiPSs and catalyze their conversion [139].Typically, when one component had good adsorption performance and the other component possessed excellent catalytic activity, the adsorption-diffusion-catalysis process of LiPSs could be completed smoothly across the heterostructure interface, thus boosting the redox kinetic, as shown in Fig. 9c, such as MoO 2 -Mo 2 N [140], MoS 2 -MoN [141], and Nb 4 N 5 -Nb 2 O 5 [142].
In addition to combining the advantages or complementing disadvantages of different TMCs, heterostructure composites can also balance the contradictions between them.Considering that too weak interaction is not conducive to interfacial charge transfer, and too strong interaction may hinder it, the chemical interaction should be moderate and balanced with the catalytic capacity.MoO 2 :Co 2 Mo 3 O 8 heterostructure was prepared by doping Co, in which MoO 2 possessed strong adsorption ability while Co 2 Mo 3 O 8 delivered superior catalytic property and fast Li + diffusion.To balance the interaction strength and catalytic capacity, the component of heterostructure composite was regulated by changing the cobalt content, and 9MoO 2 :2Co 2 Mo 3 O 8 achieved the dynamic balance of adsorption-diffusion-conversion, delivering the best catalytic capacity for LiPSs conversion and the smallest Li 2 S nuclear barrier [143].Similarly, the capturing capacity of WO 3 and catalytic ability of WS 2 were balanced in WS 2 -WO 3 heterostructure by tuning the sulfurization degree of WO 3 , and the LSBs with 3WO 3 :1WS 2 achieved the highest conversion efficiency [144].
Heterostructures composites can not only combine the advantages of two kinds of materials, but also possess the virtue of the interfacial effect, such as promoting charge transfer, diffusion of Li + and LiPSs as well as adsorption capacity [145].More importantly, the electronic properties of heterostructure can be optimized compared with the monomers, promoting the catalytic activity.The DOS of Co 5.47 N/ Fe 3 N heterostructures clearly showed a higher DOS value at the Fermi level than that of Co 5.47 N and Fe 3 N, indicating a superior electrical conductivity.Additionally, Co 5.47 N/Fe 3 N presented the highest binding energy with Li 2 S 6 (Fig. 9d), implying the synergistic effect at heterointerfaces [146].Heterostructure interfaces also allow rapid diffusion of LiPSs from one component to the other.V 2 O 3 /V 8 C 7 heterostructure was constructed to rapidly transfer the LiPSs strongly trapped by V 2 O 3 to V 8 C 7 through the interface, achieving efficient conversion [21].MoO 3 /MoO 2 heterostructure was synthesized by partially reducing MoO 3 and transformed the non-conductive MoO 3 into conductive MoO 2 , obtaining the defective MoO x (2 ≤ x ≤ 3) interface with abundant oxygen vacancies (Fig. 9e), which presented greater adsorption capacity with binding energy of 1.78 eV for Li 2 S 4 than that of MoO 3 (1.13eV) and MoO 2 (1.00 eV).Benefitting from the different advantages of MoO 2 and MoO x , the Li 2 S 8 electrode with MoO 3 /MoO 2 heterostructure achieved the best electrochemical properties, which could retain a capacity of 828.1 mAh g −1 at 0.5C after 500 cycles with a capacity decay rate of 0.016%, in contrast to the MoO 3 with 0.070% and MoO 2 with 0.083% [147].In addition, heterostructure interface can also provide Li 2 S nucleation sites, facilitate the nucleation and regulate the three-dimensional growth of Li 2 S to avoid the passivation of catalyst surface, increasing deposition capacity [148].Lv revealed that Li 2 S precipitated nonuniformly on the surface of Mo 2 N with thick layer and a rough morphology.Surprisingly, when small SnO 2 nanodots anchored on Mo 2 N microbelt and formed highly active heterointerfaces, the growth of Li 2 S was guided in a 3D model, avoiding surface passivation of the catalyst (Fig. 9f) [149].
Heterostructures composites with enhanced adsorption and catalytic ability can improve cathode performance compared to their components, due to higher electric conductivity with optimized energy band structures (Fig. 10a,  b), boosted interfacial charge transfer kinetics, accelerated ion diffusion, and more active sites [150,151].More importantly, the heterostructures induce internal electric fields, and the electron is redistributed as electron transfer occurs and local atoms are arranged [152,153], such as NiCo-LDH/ Co 9 S 8 (Fig. 10c).ZnS-FeS heterostructure was designed with large energy bandgap offset between ZnS (intrinsic energy bandgap of 4.9 eV) and FeS (0.8 eV).The strong built-in electric field at the heterointerface could effectively promote the charge transfer in redox reaction, thus improving catalyzing capability for LiPSs conversion [154].Electrons redistribution occurs at the binary interface and the electronic structure of the TMCs is regulated, elevating the catalytic activity and chemisorption ability [53,155].
It has been proved that it is the Fermi energy levels difference of two materials that caused built-in electric field and electrons transfer through the interface [156].A Mott-Schottky heterostructure was constructed with   1 3 redistribution at the interface could promote the adsorption and catalytic ability (Fig. 10e) [158].Qiao designed MoN-VN heterostructure, which achieved higher adsorption capacity for LiPSs than MoN, due to the regulated electronic structure.To be specific, the E p position (nearest peak to Fermi level) of the Mo of MoN-VN became higher (Fig. 10f), resulting in higher antibonding states compared with MoN [159].This was because the higher E p position, the lower antibonding orbital occupancy, leading to stronger interaction between LiPSs and catalysts [160].
The theoretical calculations for Co 3 S 4 /MnS also showed that the introduction of Mn tuned the electronic structure of Co 3 S 4 with higher E p position, contributing to more effectively adsorb LiPSs, facilitate charge transport and improve the conversion kinetics [161].
Considering that different TMCs can catalyze the reaction in different stages of LSBs, heterostructure composites can comprehensively facilitate the reaction kinetics with different catalytic activities of various TMCs.CoO/NiO heterostructure was constructed, in which NiO could accelerate the solid-liquid conversion, and CoO was more conducive to improving the liquid-solid reaction kinetics [162].For MoSe 2 @F-doped carbon@Mo 2 C heterostructure, MoSe 2 and Mo 2 C selectively catalyzed the conversion of long-chain LiPSs, and F-doped carbon tended to catalyze the reduction of short-chain LiPSs, realizing multi-step catalysis [163].Heterostructure composites can also be used as bidirectional catalyst.It was proved that a CoSe-ZnSe heterostructure could not only accelerate sulfur reduction with a reduced energy barrier of 0.43 eV compared to ZnSe (0.54 eV), but also facilitate Li 2 S decomposition with a lower oxidation energy barrier of 0.93 eV than that of ZnSe (1.04 eV), thus bidirectionally catalyzing sulfur conversion reactions [151].Yang et al. designed a TiO 2 -Ni 3 S 2 heterostructure, in which strong electronic interactions was occurred between TiO 2 and Ni 3 S 2 (Fig. 10g), due to the hybridization between the p orbital of S atom of Ni 3 S 2 and the d orbital of Ti of TiO 2 (Fig. 10h).TiO 2 -Ni 3 S 2 possessed bidirectional catalytic effect, that is, TiO 2 captured LiPSs and Ni 3 S 2 catalyzed LiPSs conversion during the reduction process, and both of them showed catalytic activity for Li 2 S oxidation during charging process [164].Moreover, TiO 2 -Ni 3 S 2 as well as TiN-VN could serve as not only sulfur hosts to boost the redox of sulfur cathodes, but also lithium host to facilitate uniform lithium deposition and significantly inhibit dendrites, thus matching Li-S full-batteries with superior electrochemical performance (Fig. 10i) [165,166].
Until now, plentiful heterostructure composites have been explored, especially constructed by TMCs with same anion but different metal ions (such as MoS 2 /Ni 3 S 2 [167]) or same metal ion but different anions (such as Mn 3 O 4 -MnP x [168], Fe 9 S 10 /Fe 3 O 4 [169]).For TMCs-based heterostructure materials composed of different anion and cation, one of the compounds can be prepared first, and then another metal compound can be grown on its surface.Taking SnO 2 -Mo 2 N as an example, Mo 2 N was firstly synthesized and dispersed in water, which was then mixed with SnCl 2 •2H 2 O in a mixed solution of HCl and water, and SnO 2 -Mo 2 N was obtained by heat treating the mixture in Ar atmosphere.Heterogeneous composites with the same anion and different metal ions can be prepared by adding different metal sources at the same time, and then hydrothermal or solid phase sintering treated according to the state of the raw material (aqueous solution or solid state), and the product type can be controlled by controlling the proportion of raw materials.The MoO 2 : Co 2 Mo 3 O 8 heterostructure was obtained by drying the mixture of the ammonium molybdate solution and cobalt acetate solution, and then sintering in N 2 [143].For heterostructures with different anions of the same metal, single-component metal compounds can be prepared first, and then prepared by adjusting the sintering atmosphere, temperature and time, or sintered with chemical reagents containing the anions at high temperatures, such as adding thiourea to prepare sulfide heterojunctions.For example, MoO 2 -Mo 2 N was prepared by annealing the prepared MoO 3 in NH 3 atmosphere and passivating in O 2 /N 2 [140].Similarly, precursors containing anions of heterostructure material are synthesized, and then to prepare the heterostructure with different anions using the resulting gas during high-temperature sintering.For example, MoO 2 , MoO 2 /MoC and MoC were synthesized by annealing the synthesized precursor Mo 3 O 10 (C 6 H 8 N) 2 •2H 2 O in Ar for 4 h at different temperatures of 600, 650, and 700 ℃, respectively [149].
Specifically, a kind of organic-inorganic heterostructure consisting of covalent triazine framework and Ti 3 C 2 MXene was constructed with covalent interfacial interaction due to the formed Ti-N bonds.This composite was imparted with dual adsorption sites supplied by lithiophilic N and sulfurophilic Ti [170].In conclusion, despite the respective advantages of heterostructure components are clearly studied, the catalytic effect and its mechanism of heterostructure interface itself should be further deeply studied.Long grew Pt particles on NbC surface to bifunctionally catalyze the redox of sulfur cathodes.Specifically, NbC was likely to adsorb LiPSs and Pt promoted their conversion, while both NbC and Pt could catalyze Li 2 S decomposition [171].However, in their another study, the mixture of Pt and Nb 2 O 5 without heterostructure interface could also play bifunctional catalytic roles similar to Pt and NbC [172].Similarly, the mixture of metal-based catalysts without heterostructure could also improve the adsorption ability and catalytic effect, such as Co mixed with Mo 2 C [173], Co@CoO core-shell structure [174], TiO 2 @TiN [175].Unfortunately, the roles of the heterostructure interfaces and their catalytic mechanism are unclear.Moreover, the effect of different components on the catalytic ability of heterostructures should be studied, such as MO x -MXene (M: Ti, V and Nb) heterostructures [176].And the types of the interface are lack of regulation and study, such as coherent interface or semi-coherent interface [177], amorphous/crystalline heterostructure [178].In addition, the content regulation and heterostructure distribution should be paid more attention, such as continuous interface [179].And the heterostructures constructed with more than two materials has not been developed in LSBs, such as ternary heterostructures, which are of great significance for well-designed sulfur catalysts [180].Meanwhile, the morphology of heterostructure materials should also be considered, such as lychee-like TiO 2 @TiN hollow spheres [181], Co-Co 3 O 4 hierarchical array nanostructure [182].

Conclusion and Prospects
In conclusion, the research progress of the superiorities of TMCs modified with multiple cations/anions and TMCsbased heterostructure composites as catalysts in LSBs have been comprehensively discussed.The main points are summarized as follows: 1.The three kinds of modification strategies all can boost the catalytic effect by providing more active sites and regulating the electronic structure.These advantages eventually endow LSBs with improved cathode performance, as summarized in Table 1, including specific capacity, cycle stability and rate performance.
The d-band center of the metal sites is widely considered to be an effective descriptor of adsorption strength and catalytic activity as the metal sites are the catalytic center.The shift of the d-band center of metal toward the Fermi level increases the probability of electrons filled in the antibonding orbital between metal and adsorbed molecules, which boosts the adsorption ability for sulfur species, while the decrease in d-band center weakens the adsorption strength.Moreover, the relationship between catalytic performance and adsorption strength presents volcano plot.In other words, the adsorption strength is enhanced with the increase in d-band center in a certain range, and too strong adsorption is not conducive to the LiPSs conversion.On the other hand, smaller d-p gap means a reduced energy gap between the bonding and antibonding orbitals, thus facilitating the interfacial electron transfer and the conversion of LiPSs.However, the upward shift of d-band center does not mean that the d-p gap becomes larger, because the introduction of metal ions into TMCs also adjusts the p-band center [183].Therefore, for TMCs containing anions, considering that the energy of the electrons in the p and d orbitals will directly affect bond formation and breaking, the p-band center of the nonmetallic site should be considered along with the d-band center.
At present, modification with metal ions has been extensively studied, including the factors that improve the catalytic performance (such as d-band center, d-band electron filling, valence state, vacancies, and lattice distortion) and the corresponding characteristics of doped ions, i.e., electronegativity, d electron numbers, electron donating ability, doping amount, doping site.Nevertheless, anion modification is not as widespread as cationic modification, and there is still a large space for anions modification.And the other electron structure such as spin polarization, p-band center d-p gap, are also of great significance need to be discussed.Most importantly, the standard descriptor for an excellent catalyst should be determined.Furthermore, the structure-activity relationships between electronic structure, crystal structure and catalytic effect of catalysts are worth further study.Taking d-band center as an example, considering that too strong adsorption will hinder the further transformation of LiPSs, the appropriate ranges of the d-band center of the catalyst with the best catalytic activity and the corresponding binding energies as well as surface diffusion properties for various LiPSs should be given, to better compare catalyst performance and facilitate the design of catalysts for LSBs.In addition, the influence of characteristics of the introduced ionic elements on the catalytic effect should be quantified.For example, the quantitative relationship  between electronegativity values should be studied in depth, d electron numbers of metal elements, p electron numbers of nonmetallic elements and catalytic performance, rather than merely showing that they have an effect on the catalytic activity.Different modifications may present different advantages, so composite modifications should be developed to comprehensively improve the performance of sulfur catalysts.This can include constructing compounds with both multi-metals and multi-anions, doping heterostructure composites, compositing bimetallic TMCs and heterostructure, such as N-doped Co 2 VO 4 -Co heterostructure [184].
Challenges remain in designing sulfur cathode materials to meet all the requirements.Therefore, it is essential to make improvements in the following aspects.(i) Strengthen the study of the effect of regulating components on the electronic/crystal structure of TMCs, and the structure-activity relationship between the electron/crystal structure and the catalytic effect of sulfur cathodes.(ii) Deepen the understanding of the catalytic mechanism in different charge and discharge stages and the relationship between chemisorption and catalysis.(iii) Pay more attention to the analysis of roles for different components and the establishment of material selection criteria.(iv) To construct multi-components catalytic materials with synergistic effect, theoretical studies are considered a highly effective approach to understand how each catalytic component works, what electronic and/or chemical properties of catalyst components play the role, and the synergistic mechanism from the atomic level, reasonably guiding the selection and match of multi-components [36].Furthermore, considering the abundance of elements and huge space to engineer the TMCs or high-entropy catalysts, machine learning should be developed to help design perfect catalysts meeting all the criteria.

Fig. 1 a
Fig. 1 a Strategies, b advances of modified transition metal compounds (TMCs) catalysts with multi-cations/anions in LSBs

Fig. 2 a
Fig. 2 a Schematic of in situ etching Mo-doped Ni 3 N by LiPSs [44].Copyright: 2022, Elsevier.b Schematic of evolution of Co-doped MoS 2 .c Relationship of the formation energies of 1 T, 2H MoS 2 and doped Co content.d Influence of Co doping on the formation energies of sulfur vacancies in MoS 2 .The catalytic effect of Co-doped MoS 2 : e Li 2 S 4 decomposition and f Li 2 S decomposition [45].Copyright: 2021, American Chemical Society.Effect of Zn doping on the catalytic effect of CoTe 2 : g S-S bond length of Li 2 S 4 and S-Li bond length of Li 2 S. h Gibbs free energies [47].Copyright: 2022, John Wiley and Sons.Effect of Cu-doped CoP: i unbalanced charge densities induced by Cu doping.j Schematic of electron transfer and variation of bond length, k Comparison of LiPSs/Li 2 S conversion barrier [54].Copyright: 2019, John Wiley and Sons

Fig. 3
Fig. 3 Relationship between catalytic activity and adsorption ability: a Schematic of doped ZnS by substituting Zn to tune the electronic structures.b Principle of regulating electronic structure by doping.c Voltage difference and peak current of the CV of symmetric cells.d Relationship of binding energies and d-band center.e Volcano diagram of reaction rates for ZnS doped with different ions (R2: LiPSs dissociation, R3: desorption steps).f Relationship of interactions and catalytic effect [51] Copyright: 2022, Springer Nature

Fig. 4
Fig. 4 Superior effect of O-doped NiCo 2 (O-S) 4 : a sulfidation process NiCo 2 (O-S) 4 and NiCo 2 S 4 .b Ratio of M 3+ /M 2+ 2p 3/2 peak intensity (I p ) and the rate of I p change.c NiCo 2 (O-S) 4 with high conductivity and LiPSs affinity greatly reserved the catalysis active surface [62].Copyright: 2022, John Wiley and Sons.Improvement of catalytic effect by N-doped CoSe 2 : d PDOS of CoSe 2 and N-CoSe 2 .e Charge number of Co in CoSe 2 and N-CoSe 2 [63].Copyright: 2020, American Chemical Society.P-doped NiTe 2−x : f Schematic illustration of P-doped NiTe 2−x at Te vacancies.g Difference of Li-Te and S-Ni bond lengths formed between LiPSs and various catalysts.h Charge density difference between Li 2 S and catalysts, the yellow (blue) distribution corresponds to charge accumulation (depletion) [65].Copyright: 2022, John Wiley and Sons

Fig. 7
Fig. 7 Synergistic catalysis of NiCo-MOF: a Binding energies.b Free energy for the discharging process.c Li 2 S decomposition energy barrier.d Calculated DOS. e Co L-edge and Ni L-edge XANES spectra of the MOFs.f Charge density difference of CoNi-MOF [104].Copyright: 2021, John Wiley and Sons.g Synergistic effect of Zn and Co sites in bimetallic Zn/Co-ZIF MOF [12].Copyright: 2022, Elsevier.h The strongest interaction obtained for FeCoNi-PBA with the increase in adsorption sites [113].Copyright: 2021, Elsevier

2 S 2 /
Li 2 S on MoN x (7.34/4.66eV) only allowed their easy deposition, while hindered the reversible catalytic conversion of LiPSs.Oxygen-modulated metal nitride (MoN x -O) were proposed to optimize the binding ability (4.54/4.33 eV for Li 2 S 2 /Li 2 S), effectively immobilizing and reversibly catalyzing LiPSs with the lowest decomposition energy barrier of 0.55 eV compared to MoO x (0.66 eV) and MoN x (0.91 eV) [125].To conduct Li + with S atoms and adsorb LiPSs with O atoms, Ce 2 O 2 S with O-Ce-S was considered to be more suitable than CeO 2 with single O-Ce.Due to the additionally formed Li-S and S-S bonds between LiPSs and Ce 2 O 2 S, Ce 2 O 2 S presented a

Fig. 8 a
Fig. 8 a XRD of rGO/MoS 2 , rGO/MoSSe and rGO/MoSe 2 .b Comparison of binding energies of LiPSs and MoS 2 , MoSe 2 , MoSSe (V).c DOS states.d, e In situ Raman characterization of cells with rGO/MoS 2 and rGO/MoSSe.f Schematic of rGO/MoSSe as a host for both sulfur and lithium.g Cycling performance at 1C [124].Copyright: 2022, American Chemical Society /doi.org/10.1007/s40820-023-01299-9© The authors positively charged CoFeP and negatively charged C 3 N 4 .The difference in Fermi levels rendered electrons transfer from C 3 N 4 to CoFeP to balance their work function at the interface.As a result, the energy bands of C 3 N 4 upward bended at the interface and an electric field formed from

C 3 N
4 to CoFeP.The charge was redistributed at the interface, promoting the catalytic activity and Li + diffusion[157].A Mott-Schottky catalysts (TiON) was also built by spontaneous oxidation of TiN due to the lower work function of TiO 2 compared to TiN (Fig.10d).The charge

Table 1
A brief summary of the improvement of cathode performance by different modified TMCs catalysts